Copper alloy  (동 및 동합금판의 기계적 성질) 번호 Temper 분류 인장시험 굴곡시험 강도시험 두께 mm 인장강도Kgf/mm2 (N/mm)2 신율 (%) 두께 mm 굴곡각도 내측반경 두께 mm Hvmin) (0.5min) C1020 C1100 C1201 C1220 C1221 Soft C1100S-O 0.5Min 30Max 20Min (196)Min 35Min 2Max 180 Close Contact - - C1100T-O 0.5Min 3Max Quarter C1100S-1/4H 0.5Min 30Max 20~28 (216~275) 25Min 0.5r Thickness 0.3Min 60~100(3) C1100T-1/4H 0.5Min 3Max HalfHard C1100S-1/2H 0.5Min 20Max 25~32 (245~314) 15Min 1.0r Thickness 75~120(3) C1100T-1/2H 0.5Min 3Max Hard C1100S-H 0.5Min 3Max 28Min (275)Min - 1.5r Thickness 80Min C1100T-H 0.5Min 3Max C1221 - C2051T-F 0.2Min 0.35Max 22~26 (216~255) 38Max - - Deep drawing 0.7mm Max 0.35Min 0.6Max 43Max C2600 C2680 C2720 Soft C2680S-O 0.3Min 1Max 28Min (275)Min 40Max 2Max 180 Close Contact - - 1Min 30Max 50Max C2680T-O 0.3Min 1Max 40Max 1Min 30Max 50Max Quarter Hard C2680S-1/4H 0.3Min 30Max 33~42 (324~412) 35Min 2Max 180 1.5r Thickness 0.3Min 75~125(3) C2680T-1/4H 0.3Min 3Max Half Hard C2680S-1/2H 0.3Min 20Max 36~45 (353~441) 28Min 2Max 180 1.0r Thickness 0.3Min 85~145(3) C2680T-1/2H 0.3Min 3Max Half C2680S-H 0.3Min 10Max 42~55 (412~539) - 2Max 1.5r Thickness 105~175(3) C2680T-H 0.3Min 3Max Very Half C2680S-EH 0.3Min 10Max 53Min (520)Min - - - - 145Min C2680T-EH 0.3Min 3Max C2801 Soft C2801S-O 0.3Min 1Max 33Min (324)Min 35Min 2Max 180 1.0r Thickness - - 1Min 30Max 40Max C2801T-O 0.3Min 1Max 35Min - - 1Min 13Max 40Max Quarter Hard C2681S-1/4H 0.3Min 30Max 36~45 (353~441) 25Max 2Max 180 1.5r Thickness 0.3Min 85~145(3) C2681T-1/4H 0.3Min 3Max Half Hard C2680S-1/2H 0.3Min 20Max 42~50 (412~490) 15Min 2Max 180 1.5r Thickness 0.3Min 105~160(3) C2680S-1/2H 0.3Min 3Max Hard C2681S-H 0.3Min 10Max 48Min (471)Min - 2Max 90 1.0r Thickness 0.3Min 130Min(3) C2681T-H 0.3Min 33Max --C3713 Quarter Hard C3713S-1/4H 0.3Min 10Max 36~45 (353~441) 18Max - - - - - C3713T-1/4H 0.3Min 2Max Half Hard C3713S-1/2H 0.3Min 10Max 43~52 (422~540) 10Max - - - - - C3713S-1/2H 0.3Min 2Max Hard C3713S-H 0.3Min 10Max 48Min (471)Min - - - - - - C3713T-H 0.3Min 2Max